Phase Reduction and Thermodynamic Analysis of Ilmenite Ore by Carbothermal-Iodination using Different Carbon Reductants

Abstract

The present study is on the combination of carbothermal reduction and iodination reaction (carboiodination) process for the phase reduction of ilmenite ore (FeTiO₃). The aim is to understand the phase reduction and thermodynamic reaction analysis of ilmenite ore by a combined method of carbothermal-iodination using different carbon reductants (graphite and palm char). Graphite was used as a standard carbon reductant while palm char as a renewable carbon reductant was prepared via the pyrolysis technique. Ilmenite was mixed with carbon reductants and then first reduced by using a carbothermal reduction process at 1550℃. Then, the reduced samples were further investigated with iodination reaction in different temperature ranges of 900-1000 °C using a vertical tube furnace with mixed argon and iodine gas (0.2 L/min). The proximate and ultimate analyses of carbon reductants were analysed by CHON analyser and their microstructure by using SEM, while XRF and XRD were used for analyzing the chemical compositions and the phase reductions of raw ilmenite ore and reduced samples, respectively. The thermodynamics of possible reactions during carbothermal-iodination reactions were calculated by HSC Chemistry 6.0 software. By comparing graphite and palm char, palm char had an amorphous structure, with porous and high carbon content showing high potential for usage as a reductant in titanium extraction from ilmenite ore. The phases of ilmenite ore were ilmenite, rutile, and anatase transformed into rutile, pseudobrookite, and titanium oxide detected by XRD. Further reduction was performed by palm char where more rutile (TiO₂) and titanium oxide (Ti₃O₅) developed from the iodination reaction at the highest temperature compared to graphite due to better properties and amorphous structure. The rutile and titanium oxide were found as stable phases from the thermodynamic analysis and confirmed with XRD. From the findings, the combination of carbothermal-iodination of ilmenite ore was possible and promising for rutile (TiO₂) production in mineral extractions.